◎ Schedule 80

size		Average outer diameter	minimum thickness	wo*ng water pressure	minimum demolition hydraulic pressure
inch	Nominal diameter	mm	mm	psi(kg/cm2)	psi(kg/cm2)
1/2"	15	21.3	3.7	850(59.8)	2720(191.4)
3/4"	20	26.7	3.9	690(48.5)	2200(154.8)
1"	25	33.4	4.6	630(44.3)	2020(142.2)
1+1/4"	32	42.2	4.9	520(36.6)	1660(116.8)
1+1/2"	40	48.3	5.1	470(33.1)	1510(106.8)
2"	50	60.3	5.5	400(28.2)	1290(90.8)
2+1/2"	65	73.0	7.1	420(29.6)	1360(95.7)
3"	80	88.9	7.6	370(26.0)	1200(84.4)
4"	100	114.3	8.6	320(22.5)	1040(73.2)
6"	150	168.3	11.0	280(19.7)	890(62.6)
8"	200	219.1	12.7	250(17.6)	790(55.6)
10"	250	273.1	15.1	230(16.2)	750(52.8)
12"	300	329.9	17.5	230(16.2)	730(51.4)

◎ Schedule 40

size		Average outer diameter	minimum thickness	wo*ng water pressure	minimum demolition hydraulic pressure
inch	Nominal diameter	mm	mm	psi(kg/cm2)	psi(kg/cm2)
1/2"	15	21.3	2.77	600(42.2)	1910(134.4)
3/4"	20	26.7	2.87	480(33.8)	1540(108.4)
1"	25	33.4	3.38	450(31.7)	1440(101.3)
1+1/4"	32	42.2	3.56	370(26.0)	1180(83.0)
1+1/2"	40	48.3	3.68	330(23.2)	1060(74.6)
2"	50	60.3	3.91	280(19.7)	890(62.6)
2+1/2"	65	73.0	5.16	300(21.1)	970(68.3)
3"	80	88.9	5.49	260(18.3)	840(59.1)
4"	100	114.3	6.02	220(15.5)	710(50.0)
6"	150	168.3	7.11	180(12.7)	560(39.4)
8"	200	219.1	8.18	160(11.3)	500(35.2)

◎ UPVC temperature damping constant 工作温度℃ 23 27 32 38 43 49 54 60 温度递减常数 1.00 0.88 0.75 0.62 0.51 0.40 0.31 0.22

◎ CPVC temperature damping constant 工作温度℃ 23-26.7 32 38 49 60 66 71 77 82 88 93 99 温度递减常数 1.00 0.92 0.82 0.65 0.50 0.47 0.40 0.32 0.25 0.22 0.20 0

注：
1.1kg/cm2 =14.223psi 1Mpa=142.86psi 1BAR=14.5PSI=0.9869大气压1psi=6.9kpa
2..以上压力定律适用于水温23℃,当温度高于23℃时，须视其材料（UPVC或 CPVC) 乘以上列温度递减常数。而水以外流体之压力定律并不全然适用上表。
3.采用法兰接合处之工作压力建议不应超过150psi(10kg/cm2),而利用螺纹（牙口）接合处之工作压力建议不应超过该尺寸对应工作压力之50%.
4.CPVC螺纹在流体温度66℃以上时不建议使用。
5.全尺寸SH40管及6"以上SC H80"管建议不可加螺纹。
6.协羽牌CPVC FG SCH40 1/2"尺寸热水管经“**化学建材测试中心”测试，水温在23±2℃时，管材爆破压力高达19.5Mpa (195.9kg/cm2)